What steel is used for extruder screws and barrels?

The most common base steel is 38CrMoAlA, known in Europe as 1.8509. Other regular grades are 34CrAlNi7 (1.8550), which nitrides deeper and harder, 31CrMoV9 (1.8519), 42CrMo which is equivalent to AISI 4140, SKD61 for hot-work duty, and stainless SS304 or SS316 for corrosion-critical applications. The base steel provides torsional strength and dimensional stability. On a correctly built part it never touches the melt, because the surface treatment does the work at the interface.

What is the difference between a nitrided and a bimetallic screw barrel?

Nitriding diffuses nitrogen into the existing steel surface, forming a hard case 0.4 to 0.7 mm deep without adding any new material. Bimetallic construction adds a genuine alloy layer bonded to the base steel: 1.0 to 1.5 mm of PTA-welded hardfacing on the screw flights, and 2.0 to 3.0 mm of centrifugally cast lining in the barrel bore. Nitriding suits clean unfilled resins at lower cost. Bimetallic suits abrasive and corrosive compounds where a thin case would be cut through quickly.

How do I choose the screw barrel material for my polymer?

Match the material to what the polymer does to metal. Clean PE, PP, PS and ABS cause neither abrasion nor corrosion, so a nitrided screw barrel serves well. Glass fibre and mineral fillers abrade, which calls for a tungsten-carbide-bearing alloy such as Colmonoy 83 on the screw. Rigid PVC corrodes because it releases hydrogen chloride, so the priority shifts to corrosion-resistant grades. Recycled feed attacks both ways at once and needs the most resistant combination available.

Is hard chrome plating better than bimetallic construction?

No, they solve different problems. Chrome plating deposits a thin layer that helps with release and mild corrosion protection, but it can flake under thermal cycling and mechanical load, and it is not a wear solution for abrasive compounds. Bimetallic construction fuses millimetres of alloy to the base steel by welding or casting, so the layer becomes part of the component and cannot peel. Choose chrome for release and light duty, bimetallic for genuine wear resistance.

Does higher hardness always mean longer screw barrel life?

No, and assuming it does leads to the wrong purchase. Hardness resists indentation, while resistance to abrasive filler comes from hard carbide particles held in a tougher matrix. Colmonoy 83 reads HRC 50 to 55, lower than Ni60 at HRC 56 to 62, yet it carries the higher anti-wear rating because it contains tungsten carbide. Corrosion resistance is a third property again, unrelated to both. Ask for hardness, composition and corrosion rating together.

When should a worn screw or barrel be reconditioned instead of replaced?

Recondition when the base steel and geometry remain sound but the wear surfaces have gone. A worn screw can be re-welded with fresh PTA hardfacing and machined back to original geometry, and a worn bore can be re-bored and re-lined by centrifugal casting. Replace instead when the shaft is bent, flight roots are cracked, the geometry never suited the compound, or so much material has been lost that re-machining would take the part below its strength envelope.

What material documents should come with a screw barrel order?

Ask for a material certificate showing the base-steel chemistry and heat number, and an inspection report recording the actual measured dimensions of your parts rather than the design values. For bimetallic construction, the alloy grade name and layer thickness should appear in writing on the quotation, not just the word bimetallic. EJS supplies a material certificate and an inspection report with every screw barrel and stamps a traceable identification number on each part.

Cad iad na hÁbhair a Úsáidtear le haghaidh Bairillí Scriú Extruder?

Foireann Theicniúil EJS· Iúil 2026 · Treoir ábhair

Freagra Díreach

Is dhá chinneadh ábhartha é gach bairille scriú easbhrúite, ní ceann amháin. Acruach bonniompraíonn sé an t-ualach meicniúil — de ghnáth 38CrMoAlA, 42CrMo nó grád dhosmálta. Acóireáil dromchlamaireann an polaiméir - cás nítrided 0.4 go 0.7 mm ar doimhneacht, nó ciseal cóimhiotal démhiotalach roinnt uaireanta níos tibhe. Faigh an bonn cruach mícheart agus flexes an chuid. Faigh an dromchla mícheart agus caitheann sé amach go luath.

Iarr ar fhormhór na soláthróirí cad as a bhfuil a gcuid scriúnna déanta agus gheobhaidh tú ceann amháin de dhá fhreagra. Ceachtar ainmniú grád lom gan aon chomhthéacs, nó an frása "cruach cóimhiotail ardchaighdeáin caitheamh-resistant," rud a chiallaíonn rud ar bith.

Ní chuidíonn ceachtar acu le ceannaitheoir cinneadh a dhéanamh. Tugann an treoir seo na gráid, cad a dtugtar orthu lasmuigh den tSín, cad a dhéanann gach cóireáil dromchla i ndáiríre leis an miotail, agus conas a mheaitseáil leis anábhar bairille scriúchuig an polaiméir a ritheann tú.

1. Base Steels agus a gCoibhéisí Idirnáisiúnta

Déanann an cruach bonn an obair struchtúrach. Seasann sé torsion ón tiomáint, lúbadh faoi ualach taobh, agus sruth tríthoiseach ag teocht. Ar chuid a tógadh i gceart ní théann sé i dteagmháil leis an leá riamh - láimhseálann an dromchla cóireáilte é sin.

Cuireann ainmniúcháin grád na Síne mearbhall ar cheannaitheoirí lasmuigh den Áise, agus ní aistríonn formhór na soláthróirí iad riamh. Seo é an léarscáiliú.

Steels bonn a úsáidtear le haghaidh scriúnna easbhrúite agus bairillí, le coibhéisí Eorpacha agus Mheiriceá. Is dlúthmheaitseáil iad coibhéisí chun críocha sonraíochta, ní ceimicí comhionanna.
grád Sínis	DIN / GA	AISI / SAM	I gcás ina n-úsáidtear é
38CrMoAlA	1.8509	Clann Nitralloy	An caighdeán tionscail. Tugann ábhar alúmanam cás nítríde eisceachtúil
34CrAlNi7	1.8550	Clann Nitralloy	Nítríde níos doimhne agus níos deacra ná 38CrMoAlA
31CrMoV9	1.8519	—	Ard-neart le friotaíocht maith tuirse
42CrMo	1.7225	AISI 4140	Cruach cóimhiotail diana ilfheidhme; comhlacht bairille coitianta
40Cr	1.7035	AISI 5140	Cásálacha bairille, comhpháirteanna ar dhleacht níos ísle
SKD61	1.2344	AISI H13	Dualgas te-oibre, teochtaí próisis ard
Cr12MoV/D2	1.2379	AISI D2	Iarratais cruach uirlis ard-chaitheamh
SS304/SS316	1.4301 / 1.4401	AISI 304/316	Seirbhís atá ríthábhachtach maidir le creimeadh

Cén fáth go bhfuil 38CrMoAlA chun tosaigh.Cruthaíonn a ábhar alúmanaim nítrídí alúmanaim thar a bheith crua le linn nítríde. Fágann an réadmhaoin aonair sin gurb é an réamhshocrú ar fud an tionscail í — tógann sé cás níos fearr ná beagnach aon rud eile, ar chostas réasúnta.

Tá soláthraí nach n-ainmníonn ach cruach amháin do gach post ag simpliú duit nó ag obair le stoc teoranta. Fiafraigh cén grád atá beartaithe acu dódodualgas agus cén fáth.

2. Cóireálacha Dromchla: Cad a Dhéanann Gach Duine I ndáiríre

Seo an áit a dhéanann teanga mhargaíochta an dochar is mó. Déantar roinnt próiseas a ghrúpáil faoi "sciath," agus níl siad inchomparáide.

Nítriding

Scaipeann nítrigin isteach sa dromchla cruach ag teocht, rud a chruthaíonn cás crua0.4 go 0.7 mm domhain. Ní chuirtear aon ábhar nua leis - déantar an cruach atá ann cheana a chlaochlú. Fanann saobhadh íseal mar go ritheann an próiseas faoi bhun na teochta claochlaithe, rud atá tábhachtach ar chuid roinnt méadar ar fad.

Láimhseálann nítriding roisín glan neamhlíonta go maith agus is lú a chosnaíonn. Is é an teorainn doimhneacht. Nuair a ghearrann filler scríobach tríd an gcás, suíonn croí-chruach níos boige thíos agus creimeadh go tapa.

Bimetallic: Dhá Phróiseas, Ní hAon

Déanann an chuid is mó de na hailt cur síos ar thógáil bimetallic amhail is dá mba phróiseas aonair an dá chuid. Tá dhá phróiseas go hiomlán difriúil i gceist, agus fios a bheith agat cé acu a insíonn duit cé acu an ndéanann soláthraí intí i ndáiríre.

Faigheann scriúnna táthú PTA.Leánn stua aistrithe plasma púdar cóimhiotail isteach ar thailte na heitilte mar choirnín táthaithe a chomhcheanglaíonn miotalóireacht leis an mbunchruach. Ansin déantar an taisce ró-mhór a mheaisíniú ar ais go dtí an chéimseata eitilte deiridh, rud a fhágann1.0 go 1.5 mmcóimhiotal go díreach san áit a mbaineann an scriú leis an tolladh.

Faigheann bairillí réitigh lártheifeacha.Déantar cóimhiotal leáite a dhoirteadh isteach sa chorp bairille sníomh; caitheann fórsa lártheifeacha é i gcoinne an bhalla istigh áit a dhaingníonn sé mar líneáil dhlúth,2.0 go 3.0 mmtiubh síos an tolladh iomlán. Ritheann an líneáil níos tiús ná an aghaidh crua scriú mar go gcosnaíonn sé i bhfad níos mó bairille a athsholáthar.

PTA hardfacing alloy welded onto extruder screw flight lands, one of the main screw barrel material treatments

Chrome plating

Taisceann cróim chrua sraith tanaí a chuidíonn le scaoileadh agus a chuireann in aghaidh creimeadh éadrom. Tá sé úsáideach do phoist ar leith. Ní réiteach caitheamh é do chomhdhúile scríobacha, toisc go bhfuil an ciseal tanaí agus is féidir le flake faoi thimthriall teirmeach agus ualach meicniúil.

Próisis a Fheicfidh Tú Fógartha — agus Cad Atá Siad

Téann roinnt ainmneacha brataithe eile ar cheannaitheoirí a dhéanann comparáid idir sleachta. Anseo tá cur síos cruinn orthu, ionas gur féidir leat na tairiscintí a fhaigheann tú a mheas.

Próisis dromchla eile le fáil sa mhargadh. Ritheann EJS nítriding, hardfacing PTA, réitigh lártheifeacha, hardening agus chrome plating; déantar cur síos anseo ar na próisis atá marcáilte mar nach bhfuil ar fáil ach chun comparáid a dhéanamh.
Próiseas	Cad é	Nóta praiticiúil
HVOF / spraeála teirmeach (WC-Co)	Púdar spraeáilte ag treoluas ard, nasctha go meicniúil	Níos tanaí ná forleagan táthaithe agus bannaithe ar bhealach difriúil.Ní thairg EJS.
Spraeála plasma	Leáigh an púdar i scaird plasma agus spraeáladh é	Ní welds iad sraitheanna spraeáilte.Ní thairg EJS.
Cumhdach léasair	Taisce cóimhiotal leáite léasair, comhleá nasctha	Uaireanta déantar cur síos mícheart air mar phróiseas tolladh bairille.Ní thairg EJS.
Líneáil ceirmeach	Muinchille ceirmeach nó sciath taobh istigh den tolladh	nideoige speisialtóireachta.Ní thairg EJS.
DLC / PVD	Scannán an-tanaí faoi thaisceadh gaile	Micrea-scála; a úsáidtear le haghaidh cuimilte, ní mórchaitheamh.Ní thairg EJS.

Bí ag faire le haghaidh earráid shonrach amháin.Déanann roinnt soláthraithe cur síos ar bores bairille mar "clad léasair" nó "plasma spraeáilte." Déantar líneálacha bairille bimetallic a tháirgeadh trí réitigh lártheifeacha. Má dhéanann luachan cur síos mícheart ar an bpróiseas bairille, iarr orthu tú a shiúl tríd a gceardlann ar fhísghlao sula ndéanann tú ordú.

3. Na Gráid Alloy Laistigh "Bimetalic"

Deimhníonn an focal "bimetalic" go bhfuil ciseal cóimhiotail ann. Tá angrádchinneann cé acu a mhaireann sé do cumaisc. Deir an chuid is mó de na soláthróirí "níicil-bhunaithe" agus stopann siad, rud a insíonn rud ar bith do cheannaitheoir - tá Ni60 agus Colmonoy 83 araon nicil-bhunaithe agus iad féin a iompar an-difriúil.

Cóimhiotail Crua-aghaidh Scriú (Tátha PTA, 1.0–1.5 mm)

cóimhiotal	Comhdhéanamh	Frith-Chaitheamh	Frith-chreimeadh	Cruas
Níl 60	Ni+Cr+Fe+Si	★★★	★★★★	HRC 56–62
Colmonoy 56	Ni+Cr+Si+Fe	★★★	★★★★	HRC 53-58
Colmonoy 83	Ni+Wc+Cr+C	★★★★	★★★★	HRC 50–55

Cóimhiotail Réitigh Bairille (Teilgthe go Lártheifeacha, 2.0–3.0 mm)

cóimhiotal	Comhdhéanamh	Frith-Chaitheamh	Frith-chreimeadh	Cruas	Teocht uasta
EJS01	Fe+Ni+Cr+B	★★★	★★	HRC 58–62	≤ 400°C
EJS02	Ni+Cr+Co+B	★★	★★★	HRC 50–58	≤ 450°C
EJS03	Ni+Cr+Co+V+B	★★★	★★★	HRC 55-60	≤ 450°C
EJS04	Ni+Wc+Cr+B	★★★★	★★★	HRC 55-60	≤ 600°C

Is fiú a bheith ar an eolas faoi theorainn foilsithe amháin mar ní luann aon soláthraí eile é:Tá Ni60 rátáil le haghaidh ábhar snáithín gloine faoi 10 faoin gcéad.Os cionn sin tá an cóimhiotal lasmuigh dá dhualgas beartaithe. Is minic a iompraíonn athchúrsáil ó dhramhaíl innealtóireachta-plaisteach snáithín gloine ón gcomhdhúil bhunaidh, agus sáraíonn ceannaitheoirí an tairseach sin gan é a thuiscint.

4. Ní Cruas Friotaíocht Caith

Tiomáineann an mhíthuiscint aonair seo níos mó ceannach mícheart ná aon cheann eile.

Féach ar na táblaí thuas. Léaghthar Colmonoy 83HRC 50–55, níos ísle ná Ni60 ag HRC 56–62. Ach tá an rátáil frithchaitheamh níos airde ag Colmonoy 83.

Is é an chúis struchtúrach. Tomhaiseann cruas an fhriotaíocht in aghaidh eangú. Tagann friotaíocht do cháithníní scríobachacáithníní crua chomhdhúile leabaithe i maitrís níos déine— glacann na cairbídí an mheilt agus coinníonn an mhaitrís ina áit iad. Tá cairbíd tungstain ag Colmonoy 83, agus is é sin an fáth go n-éiríonn leis níos fearr ná cóimhiotail níos deacra i gcoinne snáithíní gloine agus líontóirí mianraí.

Is tríú maoin arís é friotaíocht creimeadh, neamhspleách ar an dá cheann eile. Is é EJS01 an cóimhiotal bairille is deacra ar an liosta agus iompraíonn sé an rátáil creimeadh is ísle, rud a fhágann gur droch-rogha é do PVC docht in ainneoin an líon cruas mórthaibhseach.

Ná ceannaigh trí chruas uimhir amháin.Tá tábhacht ag baint le trí mhaoin agus déanann siad trádáil i gcoinne a chéile: cruas, friotaíocht scríobadh, agus friotaíocht creimeadh. Iarr ar aon soláthraí na trí cinn a lua don ghrád atá beartaithe acu. Insíonn luachan a liostaíonn HRC amháin duit an ceann is lú úsáideach de na trí cinn.

Bimetallic screw with nickel-based hardfacing alloy on the flight lands, showing the working surface material — Scriú démhiotalach críochnaithe. Cé acu cóimhiotal a shuíonn ar na tailte sin, is é an tsonraíocht a chinneann saol na seirbhíse — ní an uimhir chruas amháin.

5. Roghnú Ábhar Bairille Scriú ag Polymer

Déan an t-ábhar bairille scriú a mheaitseáil leis an méid a dhéanann an polaiméir le miotail, ní le sraith chaighdeán ginearálta.

Roghnú ábhar ag polaiméir. Sa chás go n-ionsaíonn dhá mheicníocht ag an am céanna, is amhlaidh is mó a dhéanann dochar.
Polaiméir	Meicníocht ionsaí	Cruach bonn	Dromchla
Glan PE, PP, PS, ABS	Ní ceachtar	38CrMoAlA	nítrided
PVC docht	Creimeadh (scaoileadh HCl)	38CrMoAlA	Bimetalic, creimeadh-threoraithe (scriú Ni60 / Colmonoy 56, bairille EJS02 / EJS03)
Níolón gloine-líonadh, PC	Scríobadh	38CrMoAlA/34CrAlNi7	Bimetallic, grád chomhdhúile (scriú Colmonoy 83, bairille EJS01 / EJS04)
Mianra nó CaCO₃-líonta	Scríobadh	38CrMoAlA	Bimetallic, grád carbide
Athchúrsáilte / iar-thomhaltóir	An dá ag an am céanna	38CrMoAlA	Bimetallic, grád carbide
Comhdhúile lasair-retardant	Creimeadh	38CrMoAlA	Bimetalic, creimeadh-threoraithe
PET (triomaithe, gan líonadh)	Éadrom	38CrMoAlA	Nítrídithe nó démhiotalacha ag brath ar aschur
Polaiméirí innealtóireachta ardteochta	Teirmeach	SKD61	Bimetalic, EJS04 rátáil go 600°C
Seirbhís atá ríthábhachtach maidir le creimeadh	Ceimiceach	SS304/SS316	De réir iarratais

Chailleann ceannaitheoirí dhá phointe. Ar dtús,ábhar filler níos mó ná an t-ainm polaiméir— is fadhbanna éagsúla caitheamh iad PP agus PP neamhlíonta le talc 30 faoin gcéad. Dara,comhaireamh regrind.Má chuirtear 15 faoin gcéad ábhar athchúrsáilte le sruth glan is féidir an post ar fad a aistriú go rang ábhair eile.

6. Athchóiriú: Nuair is féidir Ábhar a Athchóiriú

Ní chiallaíonn dromchlaí caitheamh caite cuid nua i gcónaí. Is féidir an dá phróiseas démhiotalacha a dhéanamh arís ar chomhpháirt atá ann cheana féin.

Is féidir scriú caite a ath-tháthú le héadan crua PTA úr agus é a mheaisíniú ar ais go dtí an chéimseata bunaidh eitilte. Is féidir tolladh caite a ath-leamh agus a athlíneáil le réitigh lártheifeacha. Coinníonn athchóiriú an seafta bunaidh, an eochairbhealaigh agus an iris, rud is tábhachtaí nuair a scoirtear den chuid OEM nó nuair a bhíonn an t-am luaidhe ar cheann nua fada.

Athshlánú nó ionadú — na fachtóirí cinntitheacha

Athchóiriúnuair a bhíonn an seafta díreach, d'oirfeadh an geoiméadracht an cumaisc, agus níl ach na dromchlaí caitheamh imithe
Athchóiriúnuair a scoirtear den chuid OEM nó nuair nach bhfuil an t-am luaidhe nuathógála inghlactha
Ionadaighnuair a bhíonn an seafta lúbtha nó léiríonn fréamhacha eitilte scáineadh
Ionadaighnuair nach n-oireann an chéimseata bhunaidh don roisín - is é an t-atógáil an tráth a shocraítear an dearadh
Ionadaighnuair a bheadh an oiread sin ábhair caillte go dtógfadh an t-athmheabhrú an chuid faoi bhun a gclúdach láidreachta

Is beag a chiallaíonn sonraíocht ábhar bairille scriú gan doiciméadú chun é a chruthú. Baineann trí líne le gach ordú ceannaigh.

Seicliosta sonraíochta ábhair

Grád cruach bonn, ainmnithe.Ní "cruach cóimhiotail" - 38CrMoAlA, 42CrMo, SS316, cibé acu is infheidhme
Cóireáil dromchla agus doimhneacht.Nitrided le doimhneacht cáis luaite, nó bimetallic leis anainm grád cóimhiotailagus tiús ciseal i milliméadair
Doiciméid a theastaíonn tráth an tseachadta.Deimhniú ábhair le líon teasa, agus tuarascáil iniúchta le toisí tomhaiste iarbhír

Soláthraíonn EJS deimhniú ábhartha agus tuairisc chigireachta le gach bairille scriú, agus stampálann sé uimhir aitheantais inrianaithe ar gach cuid le linn na táirgeachta. Ar an gcéad ordú le haon soláthróir, is beag an costas a bhaineann le sampla a bheith curtha go neamhspleách agus á anailísiú i gcomparáid le luach coimeádán páirteanna.

Má bhaineann an t-iarratas le bia nó teagmháil leighis,luaigh sin ag céim an fhiosrúcháinionas gur féidir an roghnúchán agus an doiciméadú bonn cruach a mheaitseáil le do chlár comhlíonta féin. Ní hionann riachtanais de réir an mhargaidh agus de réir iarratais, agus baineann siad leis an tsonraíocht seachas a bheith glactha.

Oibríonn EJS trasnascriú aonair, cúpla comhthreomharaguscúpla cónúilgeoiméadracht sa dánítríditheagusdémhiotalachatógáil, le nítriding, táthú PTA agus réitigh lártheifeacha ar fad a dhéantar go hinmheánach i monarcha Zhoushan. Chun an pictiúr ceannaigh níos leithne, féach antreoir cheannaitheora iomlán.

8. Ceisteanna Coitianta

Cén cruach a úsáidtear le haghaidh scriúnna agus bairillí easbhrúite?

Is é an cruach bonn is coitianta ná 38CrMoAlA, ar a dtugtar 1.8509 san Eoraip. Is iad na gráid rialta eile ná 34CrAlNi7 (1.8550), a dhéanann nítríd níos doimhne agus níos deacra, 31CrMoV9 (1.8519), 42CrMo atá comhionann le AISI 4140, SKD61 le haghaidh dualgas te-oibre, agus SS304 dhosmálta nó SS316 le haghaidh iarratais atá ríthábhachtach i gcreimeadh. Soláthraíonn an cruach bonn neart torsional agus cobhsaíocht tríthoiseach. Ar chuid tógtha i gceart ní théann sé i dteagmháil leis an leá riamh, toisc go ndéanann an chóireáil dromchla an obair ag an gcomhéadan.

Cad é an difríocht idir bairille scriú nítrided agus bimetallic?

Déanann nítriding nítrigin a idirleathadh isteach sa dromchla cruach atá ann cheana féin, rud a chruthaíonn cás crua 0.4 go 0.7 mm ar doimhneacht gan aon ábhar nua a chur leis. Cuireann tógáil bimetallic ciseal cóimhiotal fíor nasctha leis an mbunchruach: 1.0 go 1.5 mm de éadan crua táthaithe PTA ar na heitiltí scriú, agus 2.0 go 3.0 mm de líneáil lártheifeacha teilgthe sa tolladh bairille. Oireann nítriding roisíní glan gan líonadh ar chostas níos ísle. Oireann bimetallic comhdhúile scríobacha agus creimneach áit a ndéanfaí cás tanaí a ghearradh tríd go tapa.

Conas a roghnaíonn mé an t-ábhar bairille scriú do mo pholaiméir?

Meaitseáil an t-ábhar leis an méid a dhéanann an polaiméir le miotail. Ní chruthaíonn glan PE, PP, PS agus ABS scríobadh ná creimeadh, agus mar sin feidhmíonn bairille scriú nítrídithe go maith. Snáithín gloine agus líontóirí mianraí abrade, a éilíonn cóimhiotal tungstain-carbide-iompartha ar nós Colmonoy 83 ar an scriú. Creimeann PVC docht toisc go scaoileann sé clóiríd hidrigine, agus mar sin aistríonn an tosaíocht go gráid atá resistant le creimeadh. Ionsaíonn beatha athchúrsáilte an dá bhealach ag an am céanna agus is gá an teaglaim is resistant atá ar fáil.

An bhfuil plating crua chrome níos fearr ná tógáil bimetallic?

Ní hea, réitíonn siad fadhbanna éagsúla. Taisceann plating Chrome sraith tanaí a chuidíonn le scaoileadh agus cosaint creimeadh éadrom, ach féadann sé calcadh faoi thimthriall teirmeach agus ualach meicniúil, agus ní réiteach caitheamh é do chomhdhúile scríobacha. Déanann tógáil bimetallic milliméadar cóimhiotal a chomhleádh leis an mbonn-chruach trí tháthú nó réitigh, agus mar sin déantar an ciseal mar chuid den chomhpháirt agus ní féidir leis an craiceann. Roghnaigh chrome le haghaidh scaoileadh agus dualgas éadrom, bimetallic le haghaidh friotaíocht caitheamh fíor.

An gciallaíonn cruas níos airde saol bairille scriú níos faide i gcónaí?

Ní hea, agus ag glacadh leis go dtiocfaidh an ceannach mícheart. Seasann cruas i gcoinne eangú, agus tagann an fhriotaíocht in aghaidh filler scríobach ó cháithníní crua chomhdhúile a choinnítear i maitrís níos déine. Léann Colmonoy 83 HRC 50 go 55, níos ísle ná Ni60 ag HRC 56 go 62, ach tá an rátáil frithchaitheamh níos airde aige toisc go bhfuil cairbíd tungstain ann. Is tríú maoin arís é friotaíocht creimeadh, nach mbaineann leis an dá cheann. Iarr cruas, comhdhéanamh agus rátáil creimthe le chéile.

Cathain ar chóir scriú nó bairille caite a athchóiriú in ionad é a athsholáthar?

Athriocht nuair a fhanann an bonn-chruach agus an chéimseata slán ach go bhfuil na dromchlaí caitheamh imithe. Is féidir scriú caite a ath-tháthú le dromchla crua PTA úr agus é a mheaisíniú ar ais go dtí an chéimseata bhunaidh, agus is féidir toll caite a ath-leamh agus a ath-líneáil le réitigh lártheifeacha. Cuir in ionad ina ionad sin nuair a bhíonn an seafta lúbtha, tá fréamhacha eitilte scáinte, ní raibh an geoiméadracht oiriúnach don chomhdhúil riamh, nó cailleadh an oiread sin ábhar go dtógfadh ath-mheaisniú an chuid faoi bhun a chlúdach neart.

Cad iad na doiciméid ábhartha ba chóir teacht le hordú bairille scriú?

Iarr ar dheimhniú ábhartha a thaispeánann an cheimic bonn-chruach agus an uimhir teasa, agus tuarascáil iniúchta ina dtaifeadtar toisí tomhaiste iarbhír do chuid páirteanna seachas na luachanna dearaidh. Maidir le tógáil bimetallic, ba cheart go mbeadh an t-ainm grád cóimhiotail agus an tiús ciseal le feiceáil i scríbhinn ar an luachan, ní hamháin an focal bimetallic. Soláthraíonn EJS deimhniú ábhartha agus tuarascáil iniúchta le gach bairille scriú agus stampálann sé uimhir aitheantais inrianaithe ar gach cuid.